| 品牌 | 三菱 |
|---|---|
| 貨號(hào) | POM F30-73R1 |
| 用途 | 汽車(chē)配件 |
| 牌號(hào) | POM F30-73R1 |
| 型號(hào) | POM F30-73R1 |
| 品名 | POM |
| 外形尺寸 | 來(lái)電詢問(wèn) |
| 生產(chǎn)企業(yè) | 三菱 |
| 是否進(jìn)口 | 是 |
***三菱高流動(dòng)POM Iupital F30-73R1低氣味排放
|
Density |
1.41 |
g/cm? |
ISO 1183 |
|
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) |
27 |
g/10 min |
ISO 1133 |
|
Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) |
23 |
cm?/10min |
ISO 1133 |
|
Molding Shrinkage - Flow (3.00 mm) |
2.0 |
% |
Internal Method |
|
Water Absorption - 60% RH (23°C) |
0.22 |
% |
Internal Method |
| Mechanical |
Nominal Value |
Unit |
Test Method |
|
Tensile Modulus |
2900 |
MPa |
ISO 527-2/1 |
|
Tensile Stress (Yield) |
64.0 |
MPa |
ISO 527-2/50 |
|
Tensile Strain |
|
|
ISO 527-2/50 |
|
Yield |
7.5 |
% |
|
|
Break |
26 |
% |
|
|
Flexural Modulus 3 |
2700 |
MPa |
ISO 178 |
|
Flexural Stress 3 |
91.0 |
MPa |
ISO 178 |
| Impact |
Nominal Value |
Unit |
Test Method |
|
Charpy Notched Impact Strength (23°C) |
6.0 |
kJ/m? |
ISO 179 |
|
Charpy Unnotched Impact Strength (23°C) |
150 |
kJ/m? |
ISO 179 |
| Thermal |
Nominal Value |
Unit |
Test Method |
|
Heat Deflection Temperature |
|
|
|
|
0.45 MPa, Unannealed |
156 |
°C |
ISO 75-2/B |
|
1.8 MPa, Unannealed |
100 |
°C |
ISO 75-2/A |
|
Melting Temperature |
166 |
°C |
ISO 11357-3 |
| Flammability |
Nominal Value |
|
Test Method |
|
Flame Rating (0.8 mm) |
HB |
|
UL 94 |
 |
POM注塑工藝特性與工藝參數(shù)的設(shè)定
1、POM也是典型的熱敏性塑料，240℃下會(huì)嚴(yán)重分解。在210℃下，停留時(shí)間不能超過(guò)20min；即使在190℃下，停留時(shí)間也不能超過(guò)1h。因此注塑時(shí)，在保證物料流動(dòng)性的前提下，應(yīng)盡量選用較低的成型溫度和較短的受熱時(shí)間。
2、POM具有明顯的熔點(diǎn)，均聚POM為175℃、共聚POM為165℃。成型時(shí)，料筒溫度的分布：前段190～200℃，中段180～190℃，后段150～180℃，噴嘴溫度為170～180℃。對(duì)于薄壁制品，料筒溫度可適當(dāng)提高些，但不能超過(guò)210℃
3、POM吸濕性小，加工前樹(shù)脂可不干燥。必要時(shí)，可在90～100℃下，干燥2～4h。
4、POM的熔體粘度對(duì)剪切速率敏感。因此，要提高熔體流動(dòng)性，不能單用提高溫度，也要從提高注射速率和注射壓力著手。大澆口、厚壁短流程、小面積的制品，注射壓力為40～80MPa；一般制品為100MPa左右。小澆口、薄壁長(zhǎng)流程、大面積的制品，注射壓力較高，為120～140MPa 。
5、模具溫度通?？刂圃?0～100℃，對(duì)薄壁長(zhǎng)流程